PE Based Mono-Material Barrier Packaging Film Based Product Description
PE Based Mono-Material Barrier Packaging Film for Flexible Packaging with 12μm Film Thickness & 40cm Roll Width
This PE Based Mono-Material Barrier Packaging Film is suitable for making a wide range of flexible packaging products.
It is a food grade polymer with high barrier property that can be used for Preserved Food, Cooked Food and Frozen Food Packaging.
Our mono-material package film is coated with an organic barrier coating which meets the environmental standards. Excellent puncture resistance and High Barrier Performance against moisture and oxygen. Durable barrier performance even after repeated rubbing & bending. Performance with efficient cost structure.
The PE Based Roll Stock Film is 12μm thickness with 40cm width. Other dimensional specifications are available to meet different processing equipment requirements.
Packaging Applications & Features:
- Recyclable Flexible Packaging
- Mono Material Flexible PE Packaging Film for Food Industry Packaging Manufacturing
- For Applications for Bag, Lidding, Liner, Overwrap, Pouch or sealing sleeve packaging
Technical Parameter / Specifications
| Test items | Unit | Measure Value | Testing Standards | |
| Thickness | µm | According to Sample | GB6672-2001 | |
| Tensile Strength | Horizontal | Mpa | 27.65 | GB/T1040.3-2006 |
| Longitudinal | Mpa | 28.72 | ||
| Elongation at break | Horizontal | % | 1008.3 | GB/T1040.3-2006 |
| Longitudinal | % | 898.35 | ||
| Heat Seal strength | Side | N/15mm | 21.28 | GB/T 8808-1988 |
| Bottom cover | N/15mm | 23.21 | ||
| Peel strength | Before Cooking | N/15mm | 7.59 | QB/T 2358-1998 |
| Coefficient of Static Friction | µ | 0.178/0.253 | GB10006-1998 | |
| Oxygen Permeability | Before Steaming | cm³/m².d.0.1Mpa | <5 | GB/T1038-2000 |
| After Steaming | cm³/m².d.0.1Mpa | <2 | ||
| Water Vapor Transmission Rate (WVTR) | g/m².d | <5 | GB/T1037-1998 | |