Mono Material PE Based High-Barrier Film Product Description
Mono Material PE Based High-Barrier Film for Flexible Packaging with 18μm Film Thickness & 160cm Roll Width
This Mono Material PE Based High-Barrier Film is suitable for making a wide range of flexible packaging products.
It is made of food grade polymer with a high barrier property that is in film stock roll style. The film stock roll is 18μm thickness with 160cm width.
Our mono-material film is coated with an organic barrier coating which meets the environmental standards.
Excellent puncture resistance and High Barrier Performance against moisture and oxygen.
Durable barrier performance even after repeated rubbing & bending.
Performance with efficient cost structure.
Packaging Applications & Features:
- For Food Processing and Packaging Manufacturing Use
- High Barrier Film that can be made into wide range of packaging pouch shapes
- Suitable for Frozen Food application, Cooked Food application and Preservative Food application.
Technical Parameter / Specifications
| Test items | Unit | Measure Value | Testing Standards | |
| Thickness | µm | According to Sample | GB6672-2001 | |
| Tensile Strength | Horizontal | Mpa | 27.65 | GB/T1040.3-2006 |
| Longitudinal | Mpa | 28.72 | ||
| Elongation at break | Horizontal | % | 1008.3 | GB/T1040.3-2006 |
| Longitudinal | % | 898.35 | ||
| Heat Seal strength | Side | N/15mm | 21.28 | GB/T 8808-1988 |
| Bottom cover | N/15mm | 23.21 | ||
| Peel strength | Before Cooking | N/15mm | 7.59 | QB/T 2358-1998 |
| Coefficient of Static Friction | µ | 0.178/0.253 | GB10006-1998 | |
| Oxygen Permeability | Before Steaming | cm³/m².d.0.1Mpa | <5 | GB/T1038-2000 |
| After Steaming | cm³/m².d.0.1Mpa | <2 | ||
| Water Vapor Transmission Rate (WVTR) | g/m².d | <5 | GB/T1037-1998 | |